304L 10*1mm intemerata chalybea tubinge e sinis implicata opificem
Compositio chemica et proprietates corporis immaculatae ferro
304L 10*1mm intemerata chalybea tubinge e sinis implicata opificem
| Materia | ASTM A269 Chemical Composition % Max | ||||||||||
| C | Mn | P | S | Si | Cr | Ni | Mo | NB | Nb | Ti | |
| TP304 | 0.08 | 2.00 | 0.041 | 0.030 | 1.00 | 18.0-20.0 | 8.0-11.0 | ^ | ^ | ^ . | ^ |
| TP304L | 0.035 | 2.00 | 0.041 | 0.030 | 1.00 | 18.0-20.0 | 8.0-12.0 | ^ | ^ | ^ | ^ |
| TP316 | 0.08 | 2.00 | 0.041 | 0.030 | 1.00 | 16.0-18.0 | 10.0-14.0 | 2.00-3.00 | ^ | ^ | ^ |
| TP316L | 0.003 D | 2.00 | 0.041 | 0.030 | 1.00 | 16.0-18.0 | 10.0-15.0 | 2.00-3.00 | ^ | ^ | ^ |
| TP321 | 0.08 | 2.00 | 0.041 | 0.030 | 1.00 | 17.0-19.0 | 9.0-12.0 | ^ | ^ | ^ | 5C -0.70 |
| TP347 | 0.08 | 2.00 | 0.041 | 0.030 | 1.00 | 17.0-19.0 | 9.0-12.0 | 10C -1.10 | ^ | ||
| Materia | Calor treatment | Temperies F (C) Min. | duritia | |
| Brinell | Rockwell | |||
| TP304 | Solutio | 1900 (1040) | 192HBW/200HV | 90HRB |
| TP304L | Solutio | 1900 (1040) | 192HBW/200HV | 90HRB |
| TP316 | Solutio | 1900(1040) | 192HBW/200HV | 90HRB |
| TP316L | Solutio | 1900(1040) | 192HBW/200HV | 90HRB |
| TP321 | Solutio | 1900(1040) F | 192HBW/200HV | 90HRB |
| TP347 | Solutio | 1900(1040) | 192HBW/200HV | 90HRB |
| OD, inch | OD Tolerantia inch(mm) | WT tolerantia % | Longitudo Tolernace pollicis (mm) | |
| + | - | |||
| ≤ 1/2 | ± 0.005 ( 0.13 ) | ± 15 | 1 / 8 ( 3.2 ) | 0 |
| > 1 / 2 ~ 1 / 2 | ± 0.005(0.13) | ± 10 | 1 / 8 (3.2) | 0 |
| > 1 1 / 2 ~< 3 1 / 2 | ± 0.010(0.25) | ± 10 | 3/16 (4.8) | 0 |
| > 3 1 / 2 ~< 5 1 / 2 | ± 0.015(0.38) | ± 10 | 3/16 (4.8) | 0 |
| > 5 1 / 2 ~< 8 | ± 0.030(0.76) | ± 10 | 3/16 (4.8) | 0 |
| 8~< 12 | ± 0.040(1.01) | ± 10 | 3/16 (4.8) | 0 |
| 12~< 14 | ± 0.050(1.26) | ± 10 | 3/16 (4.8) | 0 |
Epistulam tuam hic scribe et mitte nobis